SABIC PC/ABS CH6410是高熱量,沖擊改良PC樹脂.無(wú)溴無(wú)氯阻燃,可配其它顏色.
| Property |
| TYPICAL PROPERTIES?(1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min | 640 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 550 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 5.5 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 88 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 25900 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 970 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 26500 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 95 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 | |
| Hardness, H358/30 | 100 | MPa | ISO 2039-1 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 92 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 740 | cm-kgf | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 19 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 55 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m2 | ISO 179/1eA | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 127 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 118 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 7.74E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 5.94E-05 | 1/°C | ASTM E 831 | |
| CTE, 23°C to 60°C, flow | 7.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 134 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 126 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 113 | °C | ISO 75/Ae | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.19 | - | ASTM D 792 | |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.05 - 0.07 | % | SABIC Method | |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.5 | % | SABIC Method | |
| Melt Flow Rate, 260°C/2.16 kgf | 6.3 | g/10 min | ASTM D 1238 | |
| Density | 1.2 | g/cm3 | ISO 1183 | |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 16 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 50/60 Hz | 2.7 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| Comparative Tracking Index | 225 | V | IEC 60112 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94V-1 Flame Class Rating (3) | 0.99 | mm | UL 94 | |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.49 | mm | UL 94 | |
?
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 270 - 300 | °C |
| Nozzle Temperature | 265 - 300 | °C |
| Front - Zone 3 Temperature | 265 - 300 | °C |
| Middle - Zone 2 Temperature | 260 - 300 | °C |
| Rear - Zone 1 Temperature | 260 - 300 | °C |
| Mold Temperature | 60 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
東積架新材料科技不僅是專業(yè)的熱塑性彈性體及工程材料原料供應(yīng)商，亦注重技術(shù)支持及全方位的解決方案，提供從設(shè)計(jì)選材、模具設(shè)計(jì)、成型加工等系列幫助，亦可為客戶量身定制各特殊性能之材料，進(jìn)而協(xié)助客戶提高產(chǎn)品竟?fàn)幜?
歡迎來(lái)電咨詢！
?
東積架實(shí)業(yè)香港有限公司
EASTAR Industry (HK)Co.,Limited
深圳市東積架新材料科技有限公司
Shenzhen EASTAR New Materials Technology Co,.LTD
貴賓熱線：唐生13430746085
Tel:0755-23156909???? Fax:0755-23156929?
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。
簡(jiǎn)繁切換