點(diǎn)擊圖片查看大圖Flame retardant, uncatalyzed Silicone Rubber Base
FEATURES
? Flame retardant (UL-94 V-0 with and without pigments)
APPLICATIONS
? Rubber parts for home electric appliances
? Anode caps
TYPICAL PROPERTIES1
Specification Writers: These values are not intended for use in preparing specifications. Please contact your local XIAMETER? sales representative prior to writing specifications on this product.
Test Method*
Property
Unit
Value
As supplied
CTM 0176
Appearance
White
JIS K 6249
Plasticity
mm/100
258
As cured
JIS K 6249
Density
g/cm3
1.37
JIS K 6249
Hardness, JIS type A
55
JIS K 6249
Tensile strength, JIS#3
MPa
7.2
JIS K 6249
Elongation, JIS#3
%
470
JIS K 6249
modulus, JIS#3
MPa
2.1
JIS K 6249
Tear strength, crescent
N/mm
12
JIS K 6249
Tear strength, angle
N/mm
26
JIS K 6249
Compression set
(180 °C / 22 hours)
%
26
JIS K 6255
Rebound
%
57
JIS K 6249
Linear shrinkage (disc)**
%
2.7
JIS K 6249
Volume resistivity
Ohm cm
5.0 E+16
JIS K 6249
Dielectric strength
(at room temperature)
kV/mm
32
1. Properties obtained using 0.4 part of SRX 557 U and 0.5 part of RC-4 (50P) (2,5-bis(tert-butylperoxy)-2,5-dimethyl hexane, 50% masterbatch) per 100 parts of XIAMETER? RBB-6300-50 BASE on 2mm thick slabs: molded 10 minutes at 160°C (320°F) and post-cured 4 hours at 200°C (392°F).
*CTM: Corporate Test Method, copies of CTMs are available on request.
JIS: Japanese Industrial Standard.
** Linear shrinkage depends on the curing conditions such as type of curing agent, curing temperature and size of molded product.
道康寧硅膠RBB-6300-50阻燃硅橡膠 電器橡膠雜件
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。