點(diǎn)擊圖片查看大圖Rynite®FR543 BK507是一種43%玻璃纖維增強(qiáng)阻燃聚對(duì)二甲酸乙二醇酯
Rynite® FR543 BK507(PRELIMINARY)
THERMOPLASTIC POLYESTER RESIN
PET-GF43 FR(17)
CHARACTERISTICS
Regional availability
- Global
Processing
Injection Molding
Delivery form
Pellets
Additives
Flame retardant
Special characteristics
Heat stabilized or stable to heat, Flame retardant, Low Warpage
PRODUCT TEXT
Rynite® FR543 BK507 is a 43% Glass Reinforced, Flame Retardant, Polyethylene Terephthalate
PRODUCT INFORMATION
VALUE
TEST NORM
Resin Identification
PET-GF43FR(17)
ISO 1043
Part Marking Code
>PET-GF43FR(17)<
ISO 11469
RHEOLOGICAL PROPERTIES
VALUE
UNIT
TEST NORM
Molding shrinkage, parallel
0.2
%
ISO 294-4, 2577
Molding shrinkage, normal
0.8
%
ISO 294-4, 2577
Melt viscosity, @ 1000 sec-1, 250°C
200
Pa.s
ISO 11443
MECHANICAL PROPERTIES
VALUE
UNIT
TEST NORM
Tensile Modulus
15600
MPa
ISO 527-1/-2
Stress at break
160
MPa
ISO 527-1/-2
Tensile Strength
155
MPa
ASTM D 638
Strain at break
1.5
%
ISO 527-1/-2
Elongation at break
1.6
%
ASTM D 638
Flexural Modulus
16500
MPa
ISO 178
Flexural Strength
275
MPa
ISO 178
Charpy notched impact strength, 73°F
10.5
kJ/m2
ISO 179/1eA
Poisson's ratio
0.33
-
-
THERMAL PROPERTIES
VALUE
UNIT
TEST NORM
Melting temperature, 18°F/min
254
°C
ISO 11357-1/-3
RTI, electrical, 30mil
155
°C
UL 746B
RTI, electrical, 60mil
155
°C
UL 746B
RTI, electrical, 120mil
155
°C
UL 746B
RTI, impact, 30mil
155
°C
UL 746B
RTI, impact, 60mil
155
°C
UL 746B
RTI, impact, 120mil
155
°C
UL 746B
RTI, strength, 30mil
155
°C
UL 746B
RTI, strength, 60mil
155
°C
UL 746B
RTI, strength, 120mil
155
°C
UL 746B
FLAMMABILITY
VALUE
UNIT
TEST NORM
Burning Behav. at 60mil nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Burning Behav. at thickness h
V-0
class
IEC 60695-11-10
Thickness tested
0.8
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Burning Behav. 5V at thickness h
5VA
class
IEC 60695-11-20
Thickness tested
1.5
mm
IEC 60695-11-20
UL recognition
yes
-
UL 94
Glow Wire Flammability Index, 120mil
960
°C
IEC 60695-2-12
Glow Wire Ignition Temperature, 120mil
960
°C
IEC 60695-2-13
FMVSS Class
B
-
ISO 3795 (FMVSS 302)
Burning rate, Thickness 1 mm
<80
mm/min
ISO 3795 (FMVSS 302)
ELECTRICAL PROPERTIES
VALUE
UNIT
TEST NORM
Comparative tracking index
225
-
IEC 60112
Comparative tracking index
2
PLC
UL 746A
OTHER PROPERTIES
VALUE
UNIT
TEST NORM
Humidity absorption, 80mil
0.1
%
Sim. to ISO 62
Density
1790
kg/m3
ISO 1183
INJECTION
VALUE
UNIT
Drying Recommended
yes
Drying Temperature
120
°C
Drying Time, Dehumidified Dryer
4 - 6
h
Processing Moisture Content
≤0.021
%
Melt Temperature Optimum
280
°C
Min. melt temperature
270
°C
Max. melt temperature
290
°C
Max. screw tangential speed
0.2
m/s
Mold Temperature Optimum
110
°C
Min. mold temperature
100
°C
Max. mold temperature
1202
°C
Hold pressure range
≥80
MPa
Hold pressure time
4
s/mm
Back pressure
As low as possible
MPa
Ejection temperature
170
°C
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。